PMC Flex 16.7g Mitsubishi Precious Metal Clay Silver Art Clay, 15g Silver Weight

This pack of Precious Metal Clay Flex (PMC Flex) becomes silver at 700 degrees Celsius with only a 10-18% shrinkage rate after sintering. This silver clay is the most easily mouldable PMC silver clay available from Mitsubishi Materials.



${ $store.getters.currentItemVariation.variation.availability.names.name }
DHL Express Courier - 3~5 Days

* Incl. VAT excl. Shipping

With this amazing PMC Flex silver art clay in 16.7 grams pack from Mitsubishi Materials, you can fabricate those jewelry and dream art pieces into reality. Made in Japan from pure silver, and is formulated to provide extra working time, this product is one of the best in the world. Unlike other kinds of PMC, this PMC Flex does not solidify easily at room temperature making it suitable for those who don't have the luxury of time finishing the clay designs in one sitting. Simple household tools can be used in shaping this PMC Flex silver clay.

This PMC Flex shrinks from about 10% to 15% just like other types of Precious Metal Clay making it appropriate for creating silver jewerly art pieces like rings, pendants, etc.

To start using the clay, spread a thin layer of olive oil to your hands. Upon completing your silver patterns and designs, add a few drops of water and pack the extra clay in plastic, so it can be reusable for the next project. Water can be used to seal joints and flatten surfaces, but be careful not to add so much. To quicken the initial drying, a lamp, hair dryer, or warming tray can be used. When you're ready and done with your silver patterns, sinter the clay to produce a pure fine-silver object, and follow the required time and temperature as seen in the table below.

Temperature (°F)Temperature (°C)Time
1290°F700°C10 mins.
1200°F650°C20 mins.
1110°F600°C30 mins.

Note: Always wash hands after using the product. Do not ingest, and keep out of the reach of children. 